制作中空玻璃设备的原片玻璃可所以无色浮法玻璃、镀膜玻璃、钢化玻璃、夹层玻璃等.应防止运用普通平板玻璃,普通平板玻璃的透明度及强度均达不到要求。上述玻璃原片有必要契合相应标准要求,经查验合格后才能运用

The original glass used in the production of hollow glass equipment can be colorless float glass, coated glass, tempered glass, laminated glass, etc. The use of ordinary flat glass should be avoided, as the transparency and strength of ordinary flat glass cannot meet the requirements. The above-mentioned glass raw materials must meet the corresponding standard requirements and can only be used after passing inspection

1、中空玻璃设备不同厂家不同批次的玻璃在切开前应先查看有无色差，将色差较大的玻璃分别用于不同的工程或不同的建筑立面中。玻璃切开尺寸应按图纸要求严格执行。

1. Before cutting, glass from different manufacturers and batches of insulated glass equipment should be checked for color differences. Glass with larger color differences should be used in different projects or building facades. The cutting size of glass should be strictly executed according to the drawing requirements.

一起操作人员应注意玻璃表面，不得有划伤、气泡等显着缺陷。铝条、插角的选用：铝条的厚度应在0.30mm~0.35mm之间，厚度应均匀一致。

Operators should pay attention to the surface of the glass and avoid any significant defects such as scratches or bubbles. Selection of aluminum strips and insertion angles: The thickness of aluminum strips should be between 0.30mm and 0.35mm, and the thickness should be uniform and consistent.

透气孔散布均匀。铝条须经阳极氧化处理或去污处理，一定要选用质量好、层次高的产品，提高铝条利用率。插角尺寸要选好，表面要擦干净。

The ventilation holes are evenly distributed. Aluminum bars must undergo anodizing or decontamination treatment, and high-quality and high-level products must be selected to improve the utilization rate of aluminum bars. The size of the insertion angle should be selected well, and the surface should be wiped clean.

中空玻璃设备

Hollow glass equipment

2、中空玻璃设备完善中空玻璃出产环境，中空玻璃在无灰尘、无溶剂污染、温度适合的环境中出产，出产车间灰尘污染会对中空玻璃密封体系各个构件的粘接效果发生很大的不利影响。

2. Hollow glass equipment improves the production environment for hollow glass. Hollow glass is produced in an environment free of dust, solvent pollution, and suitable temperature. Dust pollution in the production workshop can have a significant adverse impact on the bonding effect of various components of the hollow glass sealing system.

3、中空玻璃设备在玻璃材料给定后，比方普通平板玻璃或钢化玻璃，那么根据玻璃强度设计理论，玻璃原片的断裂强度就确定下来了。由于中空玻璃机器出产的玻璃是由两片（或两片以上）玻璃构成。

3. After the glass material is given, such as ordinary flat glass or tempered glass, the fracture strength of the original glass sheet is determined based on the glass strength design theory for insulated glass equipment. Due to the fact that the glass produced by the insulated glass machine is composed of two (or more) pieces of glass.

窑炉周边密封构成一个密封的空气层，中空玻璃在一面玻璃受到载荷作用时，受力面玻璃变形紧缩中空层气体，气体压强增大，将部分载荷传送给另一面玻璃。

The sealing around the kiln forms a sealed air layer. When one side of the hollow glass is subjected to a load, the glass on the stress surface deforms and compresses the gas in the hollow layer, increasing the gas pressure and transmitting part of the load to the other side of the glass.